VINYL ( PVC COMPOUNDS )

Medical >> Cable & Wire >> Moulding/Tubing >> Footwear >> Automotive >>
Master Batches

PRODUCT DATA SHEET

VINYL ( PVC COMPOUNDS ) - MASTER BATCHES
S. No.
NEW GRADE
PROPERTIES
Colour
SPECIFIC
GRAVITY
HARDNESS (Shore A)
THERMAL STABILITY @ 200°C
TENSILE STRENTH
ELONGATION
AT BREAK
VOLUME
RESISTIVITY
VOLATILE
LOSS @130°C/3 hrs.
RECOMMENDED
PROCESSING
TEMPRATURE


APPLICATIONS
Units
--
---
Nos.
Minutes (min)
Kg/cm2 (min)
% (min)
ohm-cm
(min)
% (max)
°C
TEST METHOD
Visual
ASTM D792
ASTM D2240
IS
5831
ASTM D638
ASTM
D638
IS
3396
KPA/QCD/
WIN-2
---
 
OLD GRADE
01
TFG-35
CMB-Blue/Red/
Yellow/Green
All Colours
1.30 ± 0.03
80 ± 3
40
110
200
1.0x1011
0.5
150-185
Wire & Cable
02
TFG-36
II-White
White
1.49 ± 0.03
80 ± 3
40
150
220
NA
1
150-185
Ecnomical Wire & Cable
03
TFG-42
II-Orange
Orange
1.33 ± 0.03
80 ± 3
40
150
220
NA
1
150-185
Ecnomical Wire & Cable
04
TFG-45
IIYellow/Red/
Green/Blue/ Violet/Grey/Black
*
1.44 ± 0.03
80 ± 3
30
140
250
NA
1
150-185
Ecnomical Wire & Cable
05
TFG-55
II-P (Pink)
Pink
1.50 ± 0.03
80 ± 3
30
140
200
NA
1
150-175
Ecnomical Wire & Cable
06
TFG-57
MB-BK-K1T (M)
Black
1.50 ± 0.03
91 ± 3
40
150
150
1.0x1011
0.5
150-190
Wire & Cable
07
TFG-60
I-Agra Cream SPL / D Cream SPL
Cream
1.32 ± 0.03
45 ± 3
10
70
350
NA
1
140-170
Footwear
08
TFG-65
I-Snow White Milky (cc)
White
1.63 ± 0.03
45 ± 3
10
70
350
NA
1
140-170
Footwear
09
TFG-70
I-Brown, I-Pink,
I-Rose
Brown/Pink/
Rose
1.38 ± 0.03
55 ± 3
15
80
280
NA
1
150-175
Footwear
10
TGF-70M
MB Air Black
Black
1.33 ± 0.03
73 ± 3
10
30
200
NA
1
150-185
Footwear

* Yellow/Red/Green/Blue/Violet/Grey/Black

Recommended dosing of above Master batches is 1-3 % .However,it depends upon the shade required.