Contact Us
 
 

Polymer & Engineering Compounds
||
VINYL || FLEX || PLENE || BATCH || XL || VA
----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
VINYL ( PVC COMPOUNDS )

PRODUCT DATA SHEET

PRODUCT DATA SHEET

VINYL ( PVC COMPOUNDS ) - CABLE & WIRE
S. No.
NEW GRADE
PROPERTIES
SPECIFIC
GRAVITY
HARDNESS
(Shore A)
THERMAL STABILITY @200°C (min)
Before Aging
Ageing
Variation after ageing
VALUME
RESISTIVITY

VOLATILE
LOSS @130°
C/3 hrs.
RECOMMENDED
PROCESSING
TEMPRATURE
CONFIRM TO STANDARD
TYPE AS PER
IS:5831:1984
APPLICATIONS
Tensile Strength
Elongation at Break 
Temp.
Time
Tensile Strength
Elongation at Break
Loss of Mass   
Unit

--
Nos.
minutes
N/mm2 (min)
% (min)
°C
No. of Days
%
%
mg/cm2 (max)
ohm-cm (min)
% (max)
°C

TEST METHOD
ASTM 
D792
ASTM D2240
IS
5831
IS 10810  (Part-7)
IS 10810  (Part-7)
  IS 10810 (Part-7)
IS 10810    (Part-7)
IS 10810     (Part-7)
IS 10810      (Part-7)
IS 3396
-KPA/QCD/
WIN-2
---
A
B
C
ST1
ST2
OLD GRADE
01
CGIA-86L
KLJ-35
1.36 ± 0.02
86 ± 2
50
18
270
80
7
± 20
± 20
1.0
0.2x1014
0.5
150-175
IS:5831:1984,
ASTM TI2&5
Soft Insulation & Sheathing
02
CGIA-88L
KLJ-22
1.31 ± 0.02
88 ± 2
80
18
250
80
7
± 20
± 20
2.0
0.8x1014
0.5
150-180
ASTM TI1
GP Insulation upto 1.1KV,Fast extrusion
03
CGIA-90L
CG-A12R
1.35 ± 0.02
90 ± 2
110
16.5
250
80
7
± 15
± 15
1.5
5.0x1014
0.5
150-180
IS:5831:1984,
ASTM TI1
GP Insulation, High speed extrusion
04
CGIA-90M
KLJ-28
1.41 ± 0.02
90 ± 2
90
18
225
80
7
± 20
± 20
1.2
0.6x1014
0.5
150-180
IS:5831:1984,
ASTM TI1
GP Sheathing & Insulation
05
CGIA-91M
KLJ-25
1.42 ± 0.02
91± 2
80
18
225
80
7
± 20
± 20
1.2
0.6x1014
0.5
150-180
IS:5831:1984,
ASTM TI1
GP Sheathing & Insulation
06
CGIB-86L
AVSS
1.30 ± 0.02
86 ± 2
130
18.5
250
100
7
± 10
± 10
2.0
0.5x1014
0.5
155-185
-
AVSS wire harnessing automobile cable
07
CGIB-94L
KLJ-01(N)
1.35 ± 0.02
94 ± 2
110
22
200
100
7
± 10
± 10
1.0
8x1014
0.5
155-190
IS:5831:1984
Insulation above 3.3 KV Rly.Signalling ,jumper wire
08
CGIB-96M
CGB3C/CGB3S
1.40 ± 0.02
96 ± 2
110
19
210
100
7
± 10
± 10
1.5
8.0x1014
0.5
155-185
IS:5831:1984
Rly. Signalling,Insulation
09
CGIC-94L
KLJ-09C
1.32 ± 0.02
94 ± 2
130
20.5
200
135
7
± 25
± 25
-
5x1014
0.5
155-190
IS:5831:1984,
ASTM TI3
Heat Resistant upto 105°C
10
CGIC-94L
KLJ-11P
1.33 ± 0.02
94 ± 2
120
19.5
225
135
7
± 25
± 35
-
0.8x1014
0.5
155-190
IS:5831:1984,
ASTM TI3
Heat Resistant upto 85°C
11
CGS1-70L
KLJ-65 N/W/G
1.35 ± 0.02
70 ± 2
50
13
300
80
7
± 20
± 20
2.0
-
0.7
155-185
IS:5831:1984
GP Sheathing
12
CGS1-84M
CG-86T
1.46 ± 0.02
84 ± 2
50
16
275
80
7
± 15
± 15
2.0
-
0.8
150-180
IS:5831:1984
GP Sheathing
13
CGS1-84M
KLJ-34
1.45 ± 0.02
84 ± 2
50
15
260
80
7
± 20
± 20
2.0
-
0.5
150-180
IS:5831:1984,
ASTM TI2
Soft Sheathing,co-axial wire
14
CGS1-88H
CG-10R
1.48 ± 0.02
88 ± 2
70
17
240
80
7
± 15
± 15
1.5
-
0.7
155-185
IS:5831:1984
GP Sheathing
15
CGS1-91M
KLJ-20
1.43 ± 0.02
91 ± 2
80
18.6
225
80
7
± 20
± 20
2.0
0.4x1014
0.5
150-185
IS:5831:1984
GP Sheathing & Insulation
16
CGS1-93H
KLJ-06/GREY
1.55 ± 0.02
93 ± 2
80
15
200
-
-
-
-
-
-
0.5
155-190
IS:5831:1984
GP Sheathing
17
CGS2-90H
CG-10
1.50 ± 0.02
90 ± 2
80
16
210
100
7
± 20
± 20
1.5
-
0.7
155-185
IS:5831:1984
HR Sheathing
18
CGFR-90*
KLJ-90FR*
1.52 ± 0.02
90 ± 2
100
18.5
200
100
7
± 20
± 20
1.5
0.4x1014
0.5
150-180
IS:5831:1984
FR Sheathing &  Insulation
19
CGFR-93 #
KLJ-93FR #
1.51 ± 0.02
93 ± 3
100
18.5
200
100
7
± 20
± 20
1.5
0.5x1014
0.5
150-180
IS:5831:1984
FR Sheathing &  Insulation
20
CGFRLS-96H**
CG-FRLS D1**
1.62 ± 0.02
96 ± 2
100
14
150
100
7
± 20
± 20
1.2
-
0.5
155-185
ASTM 2843 & 2863
Flame Retardant & Low Smoke
21
CGLT-73L
CG-1LT
1.27 ± 0.02
73 ± 2
70
15
300
100
14
± 10
± 10
2.0
-
0.3
145-175
-
Low temp.-55°C Insulation
22
CGIS-96H
CG-96A
1.58 ± 0.02
96 ± 2
30
14
180
-
-
-
-
-
-
NA
155-185
-
Inner Sheathing

CABLE & WIRE ( LEAD & CADMIUM FREE )

23
CGLCF-84M
KLJ-34 LF
1.45 ± 0.02
84 ± 2
50
15
210
80
7
± 20
± 20
2.0
-
0.5
150-185
IS:5831:1984
GP Sheathing & Insulation ,Lead & Cadmium free
24
CGLCF-88M
KLJ-20LF
1.40 ± 0.02
88 ± 2<