Polymer
& Engineering Compounds ||
VINYL
||
FLEX
||
PLENE
||
BATCH
||
XL
||
VA
| ---------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------- |
 |
EVA COMPOUNDS |
SPECIFICATIONS
OF KLJ VA COMPOUNDS |
| S.
No. |
GRADE
|
PARAMETER |
SPECIFIED
VALUES |
| 01 |
KS
40% |
a) Colour |
Accepted
Value E=1.0
|
| b) Surface
Appearance |
Should
be free from Contamination, Hard Particides
and Wavines |
| c) Expansion
at 175 ± 5 C/7Min. |
45 ±
5% |
| d) Hardness
(after expansion) Shore A |
50 ±
5% |
| 02 |
KS
60% |
a) Colour |
Accepted
Value E=1.0 |
b) Surface
Appearance |
Should
be free from Contamination, Hard Particides
and Wavines |
c) Expansion
at 175 ± 5 C/7Min. |
55 ±
5% |
d) Hardness
(after expansion) Shore A |
40 ±
5% |
|
Above grades can be made
in all colours.
APPLICATIONS
| |
Shoe
Soles |
| --» |
Chapples and EVA
Shoes |
| --»
|
Watch
Straps |
| --» |
Baggage Straps |
PROCESSING GUIDE LINE
For Listing KLJ VA, the Temperatures Recommended are
as:-
| Injection Temp |
-- |
95° C To 100°
C |
| Mould Temp |
-- |
165° To 170° C |
NB: The above are given for guidelines only and the
user is advised to set the temperatures according to
their requirement.
On request our technician can provide machine specific
parameter guidance.
ADVANTAGE
EVA footwear has attracted the consumer at large and
today it belongs to masses, because of following advantages:-
| |
KLJ
VA derives it's advantage of being very light,
and is even lighter than PU. The lightness provides
comfort to user |
|
|
Flexibility of
choosing from two different grades i.e. A 40%
expansion grade for soles with leather uppers,
carrying the plus of good abrasion resistance,
thus enhancing the life span of shoe and a 60%
expansion grade for Chappals and full EVA shoes |
| --»
|
KLJ
VA can be specifically tailor made as per customer
requirement to achieve various hardness, expansion,
abrasion etc. |