PLENE ( POLYPROPYLENE COMPOUNDS )

PRODUCT DATA SHEET
 
COMPOUNDS BASED ON
POLYPROPYLENE HOMOPOLYMERS
COMPOUNDS BASED ON
POLYPROPYLENE COPOLYMERS
PROPERTIES
TEST
METHOD
GRADES/
HPC
1020
HPC
1030
HPC
1040
HPC 1050
HPT 1020
HPT 1030
HPT 1040
HPG
1020
HPG
1030
HPM 1040
CPT 1020
CPT
1030
CPT
1040
CPW
1020
CPW
1030
 
EXTENDER
UNITS
CaCO3
CaCO3
CaCO3
CaCO3
TALC
TALC
TALC
Glass Fibre
Glass Fibre
Mica
TALC
TALC
TALC
Wollas
tonite
Wollas
tonite
FILLER
---
%
20 ± 2
30 ± 2
40 ± 2
50 ± 2
20 ± 2
30 ± 2
40 ± 2
20 ± 2
30 ± 2
40 ± 2
20 ± 2
30 ± 2
40 ± 2
20 ± 2
30 ± 2
SPECIFIC
GRAVITY
ASTM
D-792
---
1.04
1.12
1.24
1.33
1.04
1.12
1.24
1.00
1.13
1.25
1.04
1.12
1.24
1.04
1.12
MELT FLOW
INDEX
ASTM-
D-1238
GMS/10
MTS
@ 230ºC
2.16kg load
'8-12
'8-12
'8-12
'6-8
'8-12
'8-12
'8-12
3
'2-3
'8-10
'8-12
'8-12
'8-12
'6-10
'6-10
TENSILE
STRENGTH AT BRK.
ASTM-
D-638
Mpa
28-30
30-31
31-33
26-28
28-30
30-32
32-34
33-37
42-45
24-26
23-25
24-26
25-27
27-28
30-32
ELONGATION
AT BREAK
ASTM-
D-638
%
50
50
50
40
30
30
30
8
10
20
20
15
12
12
12
FLEXURAL
MODULUS
ASTM-
D-790
Mpa
2400
2700
3000
3200
2300
2800
3300
3500
5000
3700
2000
2300
2700
2800
3400
HDT at 0.45
Mpa
ASTM-
D-648
ºC
100
105
115
125
100
105
115
125
140
135
100
107
115
125
130

The above properties are indicative and represent the values as tested in our laboratories. There is no guarantee/ warranty whatsoever. Suitability of the product for particular application may be verified before use.
 
Compounds have Good Dimensional Stability, Balance between stiffness and flexibility, Excellent Mechanical Properties.
Compounds are used in Automotive Sector, Appliances, Medical, Engineering, Building, Sports and other Sectors.


This site is best viewed on Internet Explorer 6.0 + with 1024 x 768 resolution
Copyright @ 2006 K L J GROUP. All rights reserved.