PRODUCT DATA SHEET

PLASTICIZERS (PHTHALATES)

PRODUCT SPECIFICATION	TEST METHOD	DI-2ETHYL HEXYL PHTHALATE DOP (Super)	DI-ISO- DECYL PHTHALATE DIDP	BIS-2 PROPYLHEPTYL PTHALATE KANATOL -1010	DI-ISO- NONYL PHTHALATE DINP	DI-2ETHYL HEXYL PHTHALATE DOP	KANATOL -1056	KANATOL -1058	KANATOL -555	BUTYL BENZYL PHTHALATE KANATOL -4060	DI-BUTYL PHTHALATE DBP(M)	DI-n-BUTYL PHTHALATE D-n-BP	DI-ISO- BUTYL PHTHALATE DIBP	DI-ETHYL PHTHALATE DEP	DI-METHYL PHTHALATE DMP
APPEARANCE	PHYSICAL	WATERWHITECLEARLIQUID
COLOUR IN MAX HAZEN UNIT	ASTM- D-1045-86	15	20	20	20	20	20	20	20	40	20	20	20	20	20
VOLATILE LOSS (130ºC for 3 hrs. % By Mass) Max.	KLJ TM- P-11-92	0.05	0.10	0.10	0.10	0.1	0.15	0.10	0.10 (110ºC for 2 Hours)	0.10 (110ºC for 2 Hours)	0.1 (110ºC for 2 Hours)	0.1 (110ºC for 2 Hours)	0.1 (110ºC for 2 Hours)	0.2 (110ºC for 1 Hour)	0.5 (110ºC for 1 Hour)
ACIDITY % (AS ACID) BY MASS, Max.	ASTM- D-1045-86	0.0033	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.032	0.01	0.01	0.01	0.01	0.01
ACIDITY AFTER HEAT TREATMENT (1800C FOR 2 HRS.) % MASS, Max	ISI- 9591-96	0.015	0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.10 (150ºC  for 2 Hours)	0.03	0.03	0.03	0.05	0.05
HEAT STABILITY at 180ºC for 2 Hrs.	ISI- 9591-96	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR(150ºC, 2 Hrs.)	NO CHANGE IN COLOUR (150ºC  for 2 Hours)	NO CHANGE IN COLOUR	NO CHANGE IN COLOUR (150ºC, 2 Hrs.)	NO CHANGE IN COLOUR (150ºC, 2 Hrs.)	35 Hu. (150ºC, 2 Hrs.)	35 Hu. (150ºC, 2 Hrs.)
SPECIFIC GRAVITY AT 27º C	ASTM- D-1045-86	0.983 ± 0.003	0.964 ± 0.004	0.957 ± 0.004	0.973 ± 0.003	0.983 ± 0.003	0.983 ± 0.003	0.970 ± 0.976	1.030 ± 0.005	1.118 ± 0.003	1.035 ± 0.005	1.043 ± 0.002	1.035 ± 0.005	1.117 ± 0.003	1.185 ± 0.005
REFRACTIVE INDEX AT 27º C	ASTM- D-1045-86	1.486 ± 0.002	1.4845 ± 0.0015	1.4845 ± 0.0015	1.487 ± 0.003	1.486 ± 0.002	1.485 ± 0.003	1.484 ± 1.489	1.492 ± 0.002	1.521 ± 0.003	1.492 ± 0.003	1.491 ± 0.001	1.490 ± 0.004	1.5 ± 0.002	1.512 ± 0.004
ESTER VALUE (mg KOH/gm)	ASTM- D-1045-86	287 ± 3	251.5 ± 2.5	251.5  ± 2.5	267.5 ± 2.5	287 ± 3	285 ± 5	265 ± 270	350 ± 3	350 ± 6	385 ± 9	403 ± 2	402 ± 3	503 ± 3	575 ± 3
ESTER CONTENT % BY WEIGHT, Min.	ASTM- D-1045-86	99.9	99.5	99.5	99.5	99.5	99.5	99.5	99.5	98	99.5	99.5	99.5	99.5	99.5
PLASTICIZING ESTERS By GLC Min. %	KLJ TM- P-12-98	99.9	99.5	99.5	99.5	99.5	99.5	99.5	99.5	99	99.5	99.5	99.5	99.5	99.5
MOISTURE % By mass Max	ASTM- E-203	0.05	0.1	0.1	0.1	0.1	0.1	0.1	0.1	0.12	0.1	0.1	0.1	0.15	0.15
VISCOSITY at 20ºC in CPS	KLJ TM- P-13-97	82 ± 2	108 ± 2	120 ± 2	79 ± 3	82 ± 2	74 ± 3	89 ± 3	---	23 ± 2	23 ± 2	21 ± 2	34.5 ± 1.5	12 ± 2	---
BOILING AT ATM. PR (in ºC)	IS : 5298-73	386	---	251 - 254 at 7mmHG	400	386		250	---	370	---	340	327	293	282
Residual Alcohol % Max.	KLJ TM- P-12-98	0.03	0.10	0.10	0.10	0.10			0.05	0.05	0.05	0.05	0.05	0.02	0.02

APPLICATIONS:-

Footwear • Cables & Flexible PVC Films • Leather Cloth • Vinyl Flooring • Medical Equipments • Non-toxic food containers • Adhesives • Perfumes • Automobile Parts • Rubber belts • Tubes etc.

Specifications are indicative with no binding on KLJ Group.