PRODUCT DATA SHEET
PLASTICIZERS (SPECIALITY)
PRODUCT
SPECIFICATION
TEST
METHOD

DI-ISO-DECYL ADIPATE     DIDA         

 

DI-ISO-NONYL ADIPATE DINA

DI-OCTYL
ADIPATE

DOA
DI-METHYL
ADIPATE
DMA

TM 8-10   

TRI-OCTYL
TRIMELLITATE
TOTM
TRI-BUTYL
CITRATE
TBC
ACETYL
TRI-BUTYL
CITRATE
ATBC
OCTYL
STEARATE
OS
n-BUTYL
STEARATE
nBS
DI-OCTYL
SEBACATE
DOS

DI-ETHYLENE GLYCOL DI-BENZOATE KANATOL -DGB

APPEARANCE
PHYSICAL

WATERWHITECLEARLIQUID

COLOUR IN
MAX HAZEN UNIT
ASTM-
D-1045-86
40 40
30
40
100
50
50
40
60
60
40
100
VOLATILE LOSS (130ºC for 3 hrs. %
By Mass) Max
KLJ TM-
P-11-92
0.1 0.1
0.1
0.3 (110ºC
for 1 Hour)
0.10 0.10
0.40
0.40
0.20
0.20 (110ºC
for 2 Hrs.)
0.20
0.15%
ACIDITY %
(AS ACID)
BY MASS, Max.
ASTM-
D-1045-86
0.03 0.03
0.02
0.05
0.020
0.03
0.02
0.02
0.5
0.02
0.02
0.01
ACIDITY AFTER HEAT TREATMENT
(1800C FOR 2 HRS.)
% MASS, Max
ISI-
9591-96
0.05 0.05 0.04 N.A 0.05 0.05 0.03
0.03
---
---
0.03
0.04
HEAT STABILITY
at 180ºC for 2 Hrs.
ISI-
9591-96
50 50 40
50 Hu.
(150°C/2Hrs.)
NO CHANGE NO CHANGE
IN COLOUR
(150ºC, 2 Hrs.)
NO CHANGE
IN COLOUR
(150ºC, 2 Hrs.
NO CHANGE
IN COLOUR
(150ºC, 2 Hrs.)
NO CHANGE
IN COLOUR (150ºC, 2 Hrs.)
NO CHANGE
IN COLOUR
NO CHANGE
NO CHANGE
SPECIFIC GRAVITY AT 27º C
ASTM-
D-1045-86
0.9125 ± 0.0025 0.915 ± 0.01
0.924 ±
0.002
1.060 ±
0.003
0.974 ± 0.98
0.990 ±
0.005
1.042 ±
0.005
1.050 ± 0.005
0.860 ±
0.005
0.855 ± 
0.005
0.915 ±
0.005
1.170 ±
0.005
REFRACTIVE INDEX AT 27º C
ASTM-
D-1045-86
1.4525 ± 0.0075 1.450 ± 0.010
1.448±
0.002
1.427 ±
0.005
1.4855 ± 1.4865
1.4860 ±
0.003
1.4430 ±
0.003
1.4410 ±
0.003
1.445 ±
0.005
1.445 ±
0.005
1.447 ±
0.005
1.520±
0.003
ESTER VALUE  (mg KOH/gm)
ASTM-
D-1045-86
262.5 ± 2.5 281 ± 3
304 ± 2
584 ± 3
280 ± 5
306.5 ± 3.5
468 ± 3
559 ± 3
142.5 ± 2.5
162.5 ± 2.5
263 ± 3
351 ± 5
ESTER CONTENT
% BY
WEIGHT, Min.
ASTM-
D-1045-86
99 99.5
99.5
99.5
99
99
99
99
99.5
99.5
99.5
98
PLASTICIZING ESTERS
By GLC Min. %
KLJ TM-
P-12-98
99 99.5
99.5
99.5
99
99
99
99
99
99
99
99
MOISTURE %
By mass Max
ASTM-
E-203
0.1 0.1
0.1
0.4
0.10
0.1
0.3
0.25
0.1
0.1
0.1
0.1
VISCOSITY at 20ºC in CPS
KLJ TM-
P-13-97
26 ± 1 23.5 ± 1.5
14 ± 2
(at 25°C)
---
497 ± 3
274.5 ± 2.5
34 ± 1.5
34 ± 1.5
18 - 20
(at 25ºC)
11 ± 1
(at 25ºC)
61 ± 2
88 ± 2
BOILING AT ATM. PR (in ºC)
IS :
5298-73
239 at 5mmHG 228 at 5mmHG
335
--
---
---
---
---
---
343
---
240 at 5mmHG
Iodine Value Max.
British Pharm.-88
--- ---
---
---
---
---
---
---
2.5 
2.5 PPM
---
---

APPLICATIONS:-

Footwear • Cables & Flexible PVC Films • Leather Cloth • Vinyl Flooring • Medical Equipments • Non-toxic food containers • Adhesives • Perfumes • Automobile Parts • Rubber belts • Tubes etc.


Specifications are indicative with no binding on KLJ Group.

This site is best viewed on Internet Explorer 6.0 + with 1024 x 768 resolution
Copyright @ 2006 K L J GROUP. All rights reserved.