FLEX ( THERMOPLASTIC RUBBER COMPOUNDS - TPR ) >> FLEX ( THERMOPLASTIC ELASTOMER COMPOUNDS - TPE )

PRODUCT DATA SHEET

TYPE
PROPERTIES
HARDNESS
SPECIFIC
GRAVITY
TENSILE
STRENGTH
ELONGATION
AT BREAK
TEAR
STRENGTH
ABRASION
MFI
FLEXING
Units
Shore A
---
Kg/cm2 (min)
% (min)
Kg/cm
mm3
gm/10 min
No of Cycles
METHOD GRADE/ TEST
ASTM-2240
ASTM-792
ASTM D-638
ASTM D-638
ASTM D-1004
DIN-53516
ASTM D-1238
BENNEWERT SATRA PM-161
TRANSPARENT GRADES
STR50
STR60
STR70
50 ± 2
60 ± 2
70 ± 2
0.94 ± 0.01
0.94 ± 0.01
0.94 ± 0.01
65 ± 3
70 ± 3
75 ± 3
700 ± 50
700 ± 50
700 ± 50
30
35
35
150-200
150-200
150-200
min 35
min 35
min 35
min 30000
min 30000
min 30000
HONEY
S-5020 HL
S-5030 HL TR
S-6030 HL
S-2060 HL
50 ± 2
50 ± 2
60 ± 2
60 ± 2
0.95 ± 0.01
0.95 ± 0.01
0.95 ± 0.01
0.95 ± 0.01
55 ± 5
55 ± 5
55 ± 5
65 ± 5
600 ± 50
600 ± 50
600 ± 50
600 ± 50
24
26
26
24
100-150
100-150
100-150
100-150
min 15
min 15
min 15
min 15
min 30000
min 30000
min 30000
min 30000
GLOSSY FINISH
S-5010
S-5535
S-6510
50 ± 2
55 ± 2
65 ± 2
0.94 ± 0.01
0.99 ± 0.01
0.94 ± 0.01
50 ± 5
50 ± 5
60 ± 5
550 ± 50
600 ± 50
650 ± 50
24
23
24
150-250
150-250
150-250
min 45
min 45
min 45
min 30000
min 30000
min 30000
LOW MATT.
MFL55
MFL60
MFL65
MFL72
55 ± 2
60 ± 2
65 ± 2
72 ± 2
0.98 ± 0.01
0.98 ± 0.01
0.98 ± 0.01
0.98 ± 0.01
50 ± 3
50 ± 3
50 ± 3
55 ± 3
500 ± 50
500 ± 50
500 ± 50
500 ± 50
24
23
25
24
150-250
150-250
150-250
150-250
min 50
min 50
min 50
min 50
min 30000
min 30000
min 30000
MEDIUM MATT.
MFM55
MFM60
MFM65
55 ± 2
60 ± 2
65 ± 2
0.97 ± 0.01
0.97 ± 0.01
0.97 ± 0.01
45 ± 3
45 ± 3
45 ± 3
500 ± 50
550 ± 50
500 ± 50
26
25
25
150-250
150-250
150-250
min 50
min 50
min 50
min 30000
min 30000
min 30000
HIGH MATT.
MFH45
MFH55
MFH60
45 ± 2
55 ± 2
60 ± 2
1.00 ± 0.01
0.96 ± 0.01
0.96 ± 0.01
45 ± 3
45 ± 3
45 ± 3
600 ± 50
600 ± 50
600 ± 50
23
22
23
150-250
150-250
150-250
min 50
min 50
min 50
min 30000
min 30000
min 30000
EXPANDABLE TPR
EXP 55/65
EXP 60/65
55 ± 2
60 ± 2
0.65 ± 0.01
0.65 ± 0.01
55 ± 3
55 ± 3
600 ± 50
600 ± 50
---
---
400-420
400-420
min 55
min 55

Compounds have Excellent Abrasion Resistance, Colorability, Good Tear Strength, Excellent Dimensional Stability, Excellent Resistant to Migration & Excellent Weather Resistance.

APPLICATIONS:-

Footwear

: Shoe Soles, safety shoes, industrial shoes, sports shoes and other related decorative accessories.
Automotive
: gaskets, seals, tubing, pipes, bushings, floor mat, profiles etc.
Modifier
: modifier for other thermoplastics.